Laser absorbing filter glass

ABSTRACT

Rare earth ions with partially filled 4f electron shells are incorporated in an amount of up to 39 mole percent oxide into a glass consisting essentially of, in mole percent, 19-31% SiO 2 , 19-31% B 2  O 3 , 10-20% Al 2  O 3 , 2-10% amounts of SiO 2  and B 2  O 3  should be greater than about 40%, and the amounts of Al 2  O 3 , ZrO 2  and Y 2  O 3  are greater than about 12%. The glass can also include about 0.1 to 5% mole percent of FeO, ZnO or both. Suitable rare earth ions include but are not limited to, Er 3+ , Nd 3+ , Dy 3+ , and Sm 3+ . Optionally, the glass can be color corrected to neutral for a wide range of illuminant sources by the addition of one or more of the following: Cr 2  O 3 , Pr 2  O 3 , Fe 2  O 3 , CuO, NiO, V 2  O 5 , Co 3  O 4  or Ti 2  O 3 . These glass compositions are useful as absorption filters. In one embodiment, the composition selectively absorbs at 1064 and 532 nm.

BACKGROUND OF THE INVENTION

This invention relates generally to glass compositions employing one or more rare earth ions, and more particularly, to absorption filters which selectively absorb at 532 nm, 1064 nm or both.

The eye's response to light, its photopic response, is most sensitive in the green region of the visible spectrum. This response is at its maximum at around 550 nm. The eye's sensitivity decreases moving towards the red or blue regions of the spectrum.

Eyewear has been developed and is worn to protect the eye from damage from laser light. For years, there have been problems with eyewear designed for lasers which emit light in the green region of the spectrum. Eyewear available to date have tended to suffer from numerous problems including, (i) suppression of photopic transmission, (ii) low optical density, (iii) color distortion resulting from the need for a broad acceptance angle, and (iv) problems with color balancing. Color balancing has proven to be difficult partially because of the eye's photopic response.

Various glasses have been employed for laser protective eyewear. These glasses have utilized a variety of different compositions.

Rare earth oxides have been incorporated into glass for the purpose of wavelength selective filters, or for narrow pass filters. In U.S. Pat. No. 4,106,857, an optical filter is disclosed which incorporates a rare earth as one of the glass constituents.

As the amount of rare earth oxide in the filter increases, there is an increase in the optical density, Consequently, with lower concentrations, the thickness of the optical element must increase for effective eye protection. It has been difficult to obtain higher concentrations, with the glass remaining stable with regard to devitrification.

However, the use of rare earth oxides in glass has been limited to no more than 25-30 mole percent. In U.S. Pat. No. 3,971,723, a glass incorporating Tb₃ O₂ as one of the constituents has been reported. These glasses do not absorb at any useful laser wavelength, particularly in the visible or in the infrared.

There have been difficulties incorporating rare earth ions in higher concentrations, particularly for glass systems made in commercial quantities. Those rare earth glass systems employed as filters have suffered the limitation in that they absorb at fixed wavelengths which are not necessarily the wavelength of interest. This is the result of their electron transitions, resulting from rearrangement of inner shell shielded 4f electrons, being fixed at specific energy levels. In glass hosts, minor shifts in position of only a few nanometers can be obtained. The sharpness of the transitions have been employed advantageously to prepare rare earth containing band pass filters.

Interference-type filters can be designed to absorb at selective wavelengths in well collimated light. A limitation is that they exhibit strong viewing angle dependence, making them unsuitable for many applications.

Absorption-type filters do not suffer from this limitation. Further, these filters can be designed to have excellent thermal, chemical and mechanical properties, as well as offering the possibility of prescription eyewear.

An immediate need exists for laser safety eyewear, such as an absorption-type filter, that is opaque at the lasing wavelength of Nd:YAG (1064 nm) and frequency doubled Nd:YAG (532 nm). Furthermore, these filters should have optical densities from 3.0 to 5.0 at practical thicknesses, and possess high luminous transmission with minimal color distortion.

SUMMARY OF THE INVENTION

Accordingly, it is an object of the invention to provide a rare earth oxide glass.

Another object is to provide a rare earth oxide glass with one or more rare earth oxides in an amount of up to 39 mole percent.

Yet another object of the invention is to provide an absorption filter which includes one or more rare earth oxides in a glass host.

Still a further object of the invention is to provide an absorption filter which selectively absorbs at 1064 and 532 nm.

Another object of the invention is to provide a glass, doped with one or more rare earth oxides, which acts to favorably shift selected wavelengths.

In one embodiment, the glass is a wavelength selective absorption-type filter and is used for protection against laser radiation at 1064 nm and 532 nm. The glass is composed essentially of, in mol percent, 19-31% SiO₂, 19-31% B₂ O₃, 10-25% Al₂ O₃, 0-10% ZrO₂, 0-10% Y₂ O₃, 25-39% of one or more rare earth oxides, where the rare earths are selected from the group Er³⁺, Nd³⁺, Dy³⁺, Sm³⁺, Ce³⁺, Pr³⁺, Ho³⁺, Yb³⁺ and Tm³⁺. In another embodiment, the glass can include about 0.1 to 5 mole percent of ZnO, FeO or both. Color correction can be achieved with the addition of one or more of the following oxides, Pr₂ O₃, Cr₂ O₃, Fe₂ O₃, CuO, NiO, Co₃ O₄, V₂ O₅, Ti₂ O₃.

Glass compositions of the invention can be employed as absorption type filters, which in turn can be used in laser protective eyewear. In one embodiment, the filter selectively absorbs at 532 nm, and may also absorb at 1064 nm. The composition of the glass is such that an optical density of greater than 3 at these wavelengths can be realized, in a filter having a thickness of about 1.5 up to 3.5 mm.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a transmission curve of an Er³⁺ glass containing 36 mole percent Er₂ O₃. The glass has a thickness of 2.3 mm and an optical density at 532 of 4.0.

FIG. 2 is a transmission curve of a Nd³⁺ glass containing 34 mole percent Nd₂ O₃. The glass has a thickness of 1.6 mm and an optical density at 532 nm of 4.0.

FIG. 3 is a transmission curve of a Dy³⁺ glass containing 35 mole percent Dy₂ O₃. The glass has a thickness of 2.5 mm and an optical density at 532 nm of 4.0.

FIG. 4 is a transmission curve of a Sm³⁺ glass containing 35 mole percent Sm₂ O₃. The glass has a thickness of 1.8 mm and an optical density at 532 nm of 4.0.

FIGS. 5a and 5b illustrate the effect of SiO₂ /B₂ O₃ on the wavelength of the ² H_(11/2) transition of Er³⁺, and the absorption coefficient at 532 nm.

FIG. 6 illustrates the region of glass formation in the ternary system, glass former (SiO₂ +B₂ O₃), glass modifier (Al₂ O₃ +ZrO₂) and rare earth (Er₂ O₃).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In one embodiment of the present invention, a glass composition is provided which consists essentially of, in mol percent, 19-31% SiO₂, 19-31% B₂ O₃, 10-25% Al₂ O₃, 0-10% ZrO₂, 0-10% Y₂ O₃ and 25-39% of one or more rare earth oxides, where the rare earth oxides are selected from, Er³⁺, Nd³⁺, Dy³⁺, Sm³⁺, Ce³⁺, Pr³⁺, Ho³⁺, Yb³⁺ and Tm³⁺. This glass is suitable for use as a wavelength selective absorption type filter for protection against laser radiation at 1064 nm and 532 nm. Color correction can be achieved with the inclusion of one or more the following oxides: Pr₂ O₃, Cr₂ O₃, Fe₂ O₃, CuO, NiO, Co₃ O₄, V₂ O₅ and Ti₂ O₃. The glass can also optionally include, in mole percent, about 0.1 to 5% ZnO, FeO or both.

With the present invention, up to 39 mole percent of one or more rare earth oxides can be incorporated into the glass composition. More preferably, the rare earth oxides are about 31 to 39 mole percent. In one embodiment, the glass composition includes up to 37 mole percent Er₂ O₃. In another embodiment, up to 39 mole percent Nd₂ O₃ is included. In yet a further embodiment, up to 39 mole percent Dy₂ O₃ is included. In another embodiment, up to 38 mole percent Sm₂ O₃ is incorporated in the glass composition. The composition is a borosilicate glass. Glass of the present invention are useful as filters for absorbing at laser wavelengths, particularly in the visual or in the infrared. Additionally, they can be made in commercial quantities. As filters, the glasses of the present invention have optical densities of about 3.0 to 6.0, and thickness of about 1.5 to 5.5 mm.

The amount of the color correction oxide included in the glass is dependent on, (i) the source of illumination, amount and type of rare earth oxide(s) present, (iii) filter thickness, and (iv) optical density.

Essential to the employment of Er³⁺ as the absorbing species at 532 nm is the discovery that under certain compositional constraints a shift in the ² H_(11/2) energy level of Er3+ from about 522 nm to as long as 531.2 nm occurs. This permits a practical filter thicknesses of about 2.0-3.5 mm to be realized for optical densities from 3.0-6.0, while retaining luminous transmissions greater than 50%. Very little shift in the ⁴ G_(7/2) energy level of Nd³⁺ located at about 529 nm is observed with the composition, but the broadening of the absorption band is sufficient to give optical densities greater than 6.0 at 532 nm with luminous transmission ranging from 15-30% for a section 2.1 mm thick.

Six transitions associated with the ⁶ H_(7/2) energy level of Dy³⁺ from 1066.1-1110.2 nm are smeared into a broad band centered at 1083 nm. The resulting optical element has an optical density at 1064 nm greater than 4.0 with luminous transmission greater than 80% for a section 2.2 mm thick. The transitions associated with the ⁶ F_(9/2) energy level of Sm³⁺ are smeared into a broad band centered around 1074 nm. The resulting optical element has an optical density at 1064 nm greater than 4.0 with luminous transmission greater than 75% for a section 1.8 mm thick. Transmission curves for glasses containing high percentage of the rare earth oxides are given in FIGS. 1-4.

The concentration of Er₂ O₃ in the glass is about 25-38 mole percent. Preferably, the concentration is greater than about 30 but does not exceed 38 mole percent. More preferably, the concentration is about 37 mole percent or less. Below 25 mole percent, insufficient shift and broadening of the ² H_(11/2) energy level absorption band occurs. Above 37 mole percent Er₂ O₃, the glass is unstable with respect to devitrification.

Concentration of the Nd₂ O₃ in the glass is about 25 to 39 mole percent. Preferably, it is greater than about 30 but does not exceed 39 mole percent. Below 25 mole percent, insufficient broadening of the ⁴ G_(7/2) energy level absorption band occurs. Above 39 mole percent Nd₂ O₃, the glass is unstable with respect to devitrification.

Concentration of the Dy₂ O₃ in the glass is about 25 to 39 mole percent. Preferably, it is greater than 30 but does not exceed 39 mole percent. Below 25 mole percent, insufficient broadening of the ⁶ H_(7/2) energy level absorption band occurs. Above 39 mole percent Dy₂ O₃, the glass is unstable with respect to devitrification.

The concentration of the Sm₂ O₃ in the glass is about 25 to 38 mole percent. Preferably, the concentration is greater than 30 but does not exceed 38 mole percent. More preferably, the concentration is 38 mole percent or less. Below 25 mole percent, insufficient broadening of the ⁶ F_(9/2) energy level absorption band occurs. Above 38 mole percent Sm₂ O₃, the glass is unstable with respect to devitrification.

In order to allow sufficient solubility of the rare earth ion, the ratio of glass formers, SiO₂ and B₂ O₃, is maintained between about 0.8 to 1.4. The total of SiO2 and B2O3 in the glass is about 40-65 mole percent. The absorption band associated with the ² H_(11/2) energy level of Er³⁺ is shifted in position, intensity and sharpness as a function of SiO₂ /B₂ O₃. As a consequence, the absorption at 532 nm is strongly affected. This trend is shown in FIG. 5.

Sufficient amounts of Al₂ O₃ and ZrO₂ are added to lower the liquidus temperature and increase the viscosity at the liquidus temperature. The total of Al₂ O₃ +ZrO₂ in the glass is about 12-30 mole percent. Y₂ O₃ can be incorporated in place of Al₂ O₃ and ZrO₂ up to about 12 mole percent. This, however, tends to limit the solubility of the rare earth ion to approximately 30 mole percent. The incorporation of Y₂ O₃ shifts the ² H_(11/2) energy level of Er³⁺ to longer wavelengths (531.2 nm), and sharpens the absorption band considerably.

FIG. 6 shows the region of glass formation in the ternary system consisting of, glass former (SiO₂ +B₂ O₃), glass modifier (Al₂ O₃ +ZrO₂) and rare earth (Er₂ O₃).

Oxides of the alkali and alkali-earths can be incorporated in the glass composition. It is desirable to remove substantially all unnecessary components from the glass to make as much room as possible for the rare earth ions.

Four methods exist for suppression at 1064 nm, (i) interference coatings, (ii) ferrous iron incorporated into an alumino-phosphate glass, (iii) ferrous iron incorporated into the rare earth borosilicate glass, and (iv) using the rare earth oxides of Dy³⁺ or Sm³⁺ in the host borosilicate glass.

It is advantageous to incorporate a mechanism for absorption at 532 nm with a mechanism for absorption at 1064 nm. Table I lists fourteen possible combinations of mechanisms.

If FeO is incorporated into the rare earth borosilicate glass, ZnO is added to prevent the formation of FeS, the tendency to form ZnS, which is colorless, being more favorable than the tendency to form FeS, which is dark brown. ZnO can be incorporated up to about 5 mole percent without difficulty, but about 1-2 mole percent is preferable. To maintain high luminous transmission, a high value of SiO₂ /B₂ O₃ is desirable, resulting in a shift of the broad infrared absorption band of the ferrous ion to longer wavelengths and an intensification of the absorption at 1064 nm. The result is a need for less FeO addition. FeO can readily be incorporated in an amount of about 0.1 to 5 mole percent, but a range of about 1.8-2.3 mole percent is desirable to give similar values of optical density at 532 nm (from Er³⁺ or Nd³⁺) and 1064 nm (from the ferrous ion).

METHOD FOR MAKING GLASS

The borosilicate glass of the invention can be prepared using conventional glass making techniques. See, for example Silicate Glass Technology Methods, Babcock, C., John Wiley & Sons, 1977. Chapter 19, incorporated herein by this reference. The glasses are made in commercial quantities, greater than one liter. Starting materials can be oxides, carbonates or nitrates. The raw materials are mixed and fired in platinum or alumina crucibles at about 1450°-1500° C. for several hours, bubbled with argon, nitrogen or oxygen, or stirred to promote good homogeneity. They are then cast at about 1350°-1420° C. In the case of the FeO containing rare earth borosilicate glass, the Fe²⁺ can be added as ferrous oxalate, magnetite or ferric oxide. Reduction is carried out by bubbling a reducing gas through the melt and maintaining a reducing or neutral atmosphere. It is necessary to prevent the over reduction of the ferrous ion to the metallic iron, as this imparts a grey turbidity to the glass and can act as nucleation site for crystallization from the melt. It is equally important to maintain as low of a concentration of ferric ions in the melt because the ferric ion absorbs strongly in the visible. The temperature of the melt, and the partial pressure of oxygen in and above the melt, determine the ratio of the ionic specie, Fe°/Fe²⁺ /Fe³⁺.

These glasses are characterized by excellent chemical durability in water, acids and bases. SiO₂, ZrO₂, and ZnO improve durability in acids. B₂ O₃, Al₂ O₃ and ZnO improve durability in water. ZrO₂ and ZnO improve durability in bases. They possess high hardness, T_(g) greater than 760° C., expansion coefficients less than 45×10⁻⁷ /°C., and high refractive indices, approximately 1.73. They are not susceptible to radiation bleaching.

Table I is a summary of color balancing certain rare earth glass compositions of the invention.

                  TABLE I                                                          ______________________________________                                         MECHANISMS FOR ABSORBING AT 532/1064                                           IN A SINGLE OPTICAL ELEMENT                                                                           IONS FOR                                                METHOD  ELEMENTS       COLOR CORRECTION                                        ______________________________________                                         1.      Er.sup.3+  + dielectric                                                                       Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                  coating                                                                2.      Er.sup.3+  + FeO glass                                                                        (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                               (laminated)                                                            3.      Er.sup.3+ /FeO glass                                                                          (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                       4.      Nd.sup.3+  + dielectric                                                                       (Ni.sup.2+, Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                    coating                                                                5.      Nd.sup.3+  + FeO glass                                                                        (Ni.sup.2+, Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                    (laminated)                                                            6.      Nd.sup.3+ /FeO glass                                                                          (Ni.sup.2+, Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)            7.      Er.sup.3+  + Dy.sup.3+                                                                        Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup. 3+)                 (laminated)                                                            8.      Er.sup.3+ /Dy.sup.3+  glass                                                                   Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)          9.      Er.sup.3+  + Sm.sup.3+                                                                        Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                  (laminated)                                                            10.     Er.sup.3+ /Sm.sup.3+  glass                                                                   Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)          11.     Nd.sup.3+  + Dy.sup.3+                                                                        not required                                                    (laminated)                                                            12.     Nd.sup.3+ /Dy.sup.3+  glass                                                                   not required                                            13.     Nd.sup.3+  + Sm.sup.3+                                                                        Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+, Fe.sup.3+)                  (laminated)                                                            14.     Nd.sup.3+ /Sm.sup.3+  glass                                                                   Cu.sup.2+  + (Pr.sup.3+, Cr.sup.3+,                     ______________________________________                                                                Fe.sup.3+)                                         

Table II summarizes different glass compositions of the present invention with Er2O3 present as the rare earth oxide. Each melt size was about 50 to 150 g. Constituents are expressed in mole percent. The glass did not exhibit visible crystallization upon casting.

                  TABLE II                                                         ______________________________________                                         ER.sub.2 O.sub.3 GLASSES                                                       Er.sub.2 O.sub.3                                                                     SiO.sub.2                                                                              B.sub.2 O.sub.3                                                                       Al.sub.2 O.sub.3                                                                     ZrO.sub.2                                                                            ZnO   GLASS/XTAL                              ______________________________________                                         35.   25.     23.    13.   3.    1.    GLASS                                   36.   25.     23.    11.   5.    0     GLASS                                   36.   25.     25.    11.   3.    0     GLASS                                   36.   26.     26.    10.   2.    0     GLASS                                   36.   24.     24.    11.   5.    0     GLASS                                   36.   23.     25.    11.   5.    0     GLASS                                   36.   22.     26.    11.   5.    0     GLASS                                   36.   21.     27.    11.   5.    0     GLASS                                   36.   26.     22.    11.   5.    0     GLASS                                   36.   26.     22.    13.   3.    0     GLASS                                   36.   28.     20.    11.   5.    0     GLASS                                   36.   28.     20.    13.   3.    0     GLASS                                   37.   22.     24.    15.   3.    0     GLASS                                   37.   21.5    23.5   16.   2.    0     GLASS                                   37.   22.5    24.5   13.   1.    2.    GLASS                                   ______________________________________                                    

Table III provides a summary of transmission data for various Er2O3 glasses. Each composition is expressed in mole percent. Transmission values are reported for the 532 nm wavelength, at an optical density of 4.0.

                                      TABLE III                                    __________________________________________________________________________     TRANSMISSION DATA FOR ER.sub.2 O.sub.3 GLASS COMPOSITIONS                      Er.sub.2 O.sub.3                                                                   SiO.sub.2                                                                         B.sub.2 O.sub.3                                                                    Al.sub.2 O.sub.3                                                                    ZrO.sub.2                                                                           Y.sub.2 O.sub.3                                                                     .sup.2 H.sub.11/2                                                                  t.sub.min                                                                         Y.sub.A                                                                           Y.sub.D65                                                                         Y.sub.F3                                                                          Y.sub.F11                            __________________________________________________________________________     15.0                                                                               30.0                                                                              25.0                                                                               2.0  2.0  (*)  522.0                                                                              >30.0 (*)                                                                               -26.0                                                                             R.sub.2 O                            17.3                                                                               31.5                                                                              19.3                                                                               1.8  1.5  (*)  526.0                                                                              8.74  (*)                                                                               -28.6                                                                             R.sub.2 O                            20. 70. (P.sub.2 O.sub.5)                                                                 5. (ZnO)                                                                            5. (K.sub.2 O)                                                                           524.0                                                                              6.92                                                                              62.9                                                                              55.2                                                                              69.8                                                                              55.7                                 25. 22.5                                                                              22.5                                                                               14.4 6.   9.6  528.0                                                                              3.21                                                                              37.9                                                                              40.8                                                                              54.5                                                                              35.6                                 28. 26.                                                                               26. 15.  5.   0    528.0                                                                              2.78                                                                              48.3                                                                              40.8                                                                              54.5                                                                              35.6                                 28. 31.                                                                               21. 15.  5.   0    528.0                                                                              2.83                                                                              48.8                                                                              41.2                                                                              55.0                                                                              36.0                                 28. 26.                                                                               26. 15.  0    5.   526.7                                                                              2.87                                                                              48.2                                                                              40.6                                                                              54.5                                                                              35.4                                 28. 31.                                                                               21. 15.  0    5.   527.0                                                                              2.83                                                                              50.0                                                                              42.1                                                                              56.4                                                                              36.7                                 28. 26.                                                                               21. 20.  0    5.   527.0                                                                              2.75                                                                              51.6                                                                              43.5                                                                              58.2                                                                              37.9                                 29.4                                                                               20.6                                                                              30.4                                                                               14.7 4.9  0    528.2                                                                              2.67                                                                              46.0                                                                              38.8                                                                              52.0                                                                              33.8                                 30. 22.5                                                                              22.5                                                                               12.  5.   8.   531.2                                                                              3.24                                                                              49.8                                                                              42.1                                                                              56.0                                                                              38.3                                 30. 26.                                                                               26. 13.  5.   0    527.2                                                                              2.93                                                                              52.0                                                                              43.8                                                                              58.8                                                                              38.2                                 30. 31.                                                                               21. 13.  5.   0    528.2                                                                              2.82                                                                              51.0                                                                              43.0                                                                              57.5                                                                              37.4                                 30. 27.                                                                               27. 12.  4.   0    527.8                                                                              2.75                                                                              52.3                                                                              44.1                                                                              59.0                                                                              38.5                                 32. 26.                                                                               26. 12.  4.   0    528.0                                                                              2.71                                                                              51.1                                                                              43.0                                                                              57.7                                                                              37.5                                 34. 26.                                                                               26. 11.  3.   0    528.0                                                                              2.47                                                                              51.6                                                                              43.4                                                                              58.2                                                                              37.8                                 34. 27.                                                                               27. 10.  2.   0    529.8                                                                              2.46                                                                              52.2                                                                              44.0                                                                              58.9                                                                              38.3                                 35. 25.                                                                               23. 13.  3.   1.   530.2                                                                              2.52                                                                              50.9                                                                              42.4                                                                              57.2                                                                              36.9                                 35. 24.                                                                               26. 13.  2.   0    528.2                                                                              2.45                                                                              52.4                                                                              44.3                                                                              59.0                                                                              38.4                                 35. 23.                                                                               25. 15.  2.   0    527.8                                                                              2.57                                                                              52.1                                                                              44.0                                                                              58.8                                                                              38.2                                 36. 25.                                                                               25. 11.  3.   0    529.2                                                                              2.31                                                                              51.4                                                                              43.4                                                                              57.9                                                                              37.9                                 36. 26.                                                                               26. 10.  2.   0    530.0                                                                              2.34                                                                              51.3                                                                              43.1                                                                              57.8                                                                              37.6                                 36. 24.                                                                               24. 11.  5.   0    529.8                                                                              2.45                                                                              49.6                                                                              41.6                                                                              56.1                                                                              36.2                                 36. 23.                                                                               25. 11.  5.   0    530.0                                                                              2.29                                                                              49.9                                                                              41.8                                                                              56.2                                                                              36.3                                 36. 22.                                                                               26. 11.  5.   0    529.7                                                                              2.21                                                                              51.5                                                                              43.2                                                                              57.9                                                                              37.5                                 36. 21.                                                                               27. 11.  5.   0    529.2                                                                              2.32                                                                              51.4                                                                              43.2                                                                              57.8                                                                              37.4                                 36. 26.                                                                               22. 11.  5.   0    527.4                                                                              2.21                                                                              52.2                                                                              44.1                                                                              58.6                                                                              38.1                                 36. 26.                                                                               22. 13.  3.   0    528.2                                                                              2.62                                                                              51.8                                                                              43.6                                                                              58.3                                                                              37.7                                 37. 22.5                                                                              24.5                                                                               13.  1.   2. [ZnO]                                                                            528.6                                                                              2.11                                                                              53.0                                                                              45.0                                                                              59.8                                                                              39.1                                 __________________________________________________________________________

Tables IV-A and IV-B summarize color correction of certain Er₂ O₃ glass compositions using different sources. The concentration of the constituents are in amounts sufficient to provide a neutral glass relative to a desired source. In Table IV-A, the color difference vector, r, is defined as:

    r={(u'-u.sub.s ').sup.2 +(v'-v.sub.s ').sup.2 }.sup.1/2    (1)

where (u',v') are the color coordinates of the filter, and (u_(s) ',v_(s) ') are the color coordinates of the incandescent source, A_(3200K). The lower r is in magnitude, the more neutral the glass appears.

In Table IV-B, the luminous transmission is calculated for glasses with anti-reflective coatings. The color difference vector, r, is defined as:

    r={(u'-u.sub.s ').sup.2 +(v'-v.sub.s ').sup.2 }.sup.1/2    (2)

where (u',v') are the color coordinates of the filter, and (u_(s) ',v_(s) ') are the color coordinates of the fluorescent source, F₁₁.

                  TABLE IV-A                                                       ______________________________________                                         Er.sup.3+  GLASS COLOR CORRECTED FOR SOURCE A.sub.3200K                                       [wt %]        [values for OD.sub.532nm = 4.0]                   RUN   CuO      Cr.sub.2 O.sub.3                                                                       Pr.sub.2 O.sub.3                                                                     Y (%)   r                                         ______________________________________                                         C3    0        0       0     50.0    0.0756                                    CC1   1.00     0.04    0     17.6    0.0245                                     CC11 0.443    0.019   0     13.2    0.0185                                    CC2   0.80     0.03    0     6.7     0.0066                                     CC10 0.30     0       1.36  24.3    0.0381                                    CC7   0.40     0       1.55  17.2    0.0180                                    CC8   0.30     0       1.16  15.5    0.0172                                    CC4   0.62     0       1.20  8.5     0.0063                                    ______________________________________                                    

                  TABLE IV-B                                                       ______________________________________                                         Er.sup.3+  GLASS COLOR CORRECTED FOR SOURCE F.sub.3                                            [wt %]    [values for OD.sub.532nm = 4.0]                      RUN     CuO     Pr.sub.2 O.sub.3                                                                         Y.sub.AR (%)                                                                           r                                            ______________________________________                                         C3      0       0         64.9    0.0533                                       CC21    0.048   7.00      44.9    0.0482                                       CC26    0.096   4.20      47.7    0.0462                                       CC23    0.048   14.00     34.9    0.0461                                       CC22    0.096   7.00      42.4    0.0452                                       CC47    0.144   4.20      45.0    0.0439                                       CC27    0.192   4.20      42.5    0.0408                                       CC31    0.192   5.60      40.1    0.0400                                       CC33    0.240   7.00      35.8    0.0368                                       CC30    0.288   4.20      38.0    0.0351                                       CC35    0.288   7.00      33.8    0.0340                                       CC34    0.288   8.40      32.1    0.0328                                       CC37    0.384   5.60      32.1    0.0288                                       CC44    0.432   7.00      28.7    0.0254                                       CC40    0.480   4.20      30.5    0.0252                                       CC45    0.384   9.80      24.6    0.0223                                       ______________________________________                                    

Various glass compositions of the invention were synthesized utilizing the method set forth above. As summarized in Table I, fourteen different combinations of components can be employed to yield optical elements suitable for absorption at both 532 nm and 1064 nm. These can include, for example, one or more rare earth oxides, a rare earth oxide with a dielectric coating, rare earth oxides and ions included for color balancing, rare earth oxides with FeO, and laminated structures. Additionally, a single wavelength can be blocked with the present invention. In the case of the 532 nm wavelength, Er³⁺ or Nd³⁺ are used; and Dy³⁺ or Sm³⁺ are employed for 1064 nm.

The following examples are glass compositions useful for absorption at 532 nm, 1064 nm or both. In each example, the luminous transmission was measured against the following sources:

A, B, C, D65, F2, F3, F7 and F11. CIE No.18 (E-1.2) 1970, Principles of Light Measurement, and ASTM Designation E308-85, Standard Method for Computing the Colors of Objects by Using the CIE System, both incorporated herein by reference.

The following examples of filter elements are made using the method for making glass recited above.

EXAMPLE I

A filter element for 532 nm radiation is made. It includes, in mole percent, the following constituents: 36% Er₂ O₃, 23.0% SiO₂, 25.0% B₂ O₃, 11.0% Al₂ O₃ and 5.0% ZrO₂. The composition has an optical density of 4.0 at 2.3 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   48.6   44.7   43.3 41.8 52.3  56.2 41.6 36.3                           Y.sub.AR (%)                                                                           56.1   51.6   50.0 48.3 60.3  64.9 48.0 41.9                           ______________________________________                                    

EXAMPLE II

A filter element for 532 nm radiation is produced. It incorporates, in mole percent, the following constituents: 34.0% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 11.0% Al₂ O₃ and 3.0% ZrO₂. The composition has an optical density of 4.0 at 1.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.1   19.0   21.7 18.2 17.5  17.5 19.6 33.5                           Y.sub.AR (%)                                                                           23.2   21.9   25.0 21.0 20.2  20.2 22.6 38.6                           ______________________________________                                    

EXAMPLE III

A filter element for 1064 nm radiation is made. It includes, in mole percent, the following constituents: 35% Dy₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃ and 2.0% ZrO₂. The filter has an optical density of 4.0 at 2.2 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   81.1   79.7   79.3 79.1 80.7  81.3 79.3 79.9                           Y.sub.AR (%)                                                                           93.6   92.0   91.5 91.3 93.1  93.8 91.6 92.3                           ______________________________________                                    

EXAMPLE IV

A filter element for 1064 nm radiation is made. It includes, in mole percent, the following: 35% Sm₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃ and 2.0% ZrO₂. The filter has an optical density of 4.0 at 1.8 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   78.5   76.0   75.6 75.1 77.6  78.6 75.7 79.1                           Y.sub.AR (%)                                                                           90.7   87.7   87.2 86.6 89.5  90.7 87.4 91.3                           ______________________________________                                    

EXAMPLE V

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 36% Er₂ O₃, 23.0% SiO₂, 25.0% B₂ O₃, 11.0% Al₂ O₃ and 5.0% ZrO₂, plus a broad-band interference coating to absorb at 1064 nm. The filter has an optical density of 4.0 at 2.3 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   48.6   44.7   43.3 41.8 52.3  56.2 41.6 36.3                           Y.sub.AR (%)                                                                           56.1   51.6   50.0 48.3 60.3  64.9 48.0 41.9                           ______________________________________                                    

EXAMPLE VI

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 36.0% Er₂ O₃, 23.0% SiO₂, 25.0% B₂ O₃, 11.0% Al₂ O₃, 5.0% ZrO₂ and was laminated to ferrous oxide containing phosphate glass to absorb at 1064 nm. The filter has an optical density of 4.0 at 5.3 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   47.3   42.8   40.9 40.0 50.3  54.1 39.9 34.0                           Y.sub.AR (%)                                                                           49.4   44.6   42.7 41.8 52.5  56.4 41.6 35.4                           ______________________________________                                    

EXAMPLE VII

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 32.7% Er₂ O₃ with ferrous iron (2.3% Fe₂ O₃), 24.6% SiO₂, 22.8% B₂ O₃, 13.0% Al₂ O₃, 3.5% ZrO₂, 1.0% ZnO. The filter has an optical density of 4.0 at 2.3 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.4   19.0   17.9 18.0 22.5  23.9 18.0 14.3                           Y.sub.AR (%)                                                                           23.5   21.9   20.6 20.8 25.9  27.6 20.7 16.5                           ______________________________________                                    

Example VIII

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 34.0% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 11.0% Al₂ O₃, 3.0% ZrO₂ and a broad-band interference coating to absorb at 1064 nm gives an optical density of 4.0 at 1.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.1   19.0   21.7 18.2 17.5  17.5 19.6 33.5                           Y.sub.AR (%)                                                                           23.2   21.9   25.0 21.0 20.2  20.2 22.6 38.6                           ______________________________________                                    

EXAMPLE IX

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 34% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 11.0% Al₂ O₃, 3.0% ZrO₂ and laminated to ferrous oxide containing phosphate glass to absorb at 1064 nm. The filter has an optical density of 4.0 at 4.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   18.6   17.6   19.7 17.0 16.7  16.6 18.5 32.0                           Y.sub.AR (%)                                                                           19.4   18.3   20.5 17.7 17.4  17.3 19.3 33.4                           ______________________________________                                    

EXAMPLE X

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 36% Er₂ O₃, 23.0% SiO₂, 25.0 B₂ O₃, 11.0% Al₂ O₃, 5.0% ZrO₂ and laminated to a glass that contained, as expressed in mole percent, the following: 35% Dy₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃, 2.0% ZrO₂ ; with an anti-reflective coating. The filter has an optical density of 4.0 at 4.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y.sub.AR (%)                                                                           56.0   49.8   48.0 46.3 58.5  63.0 46.2 40.7                           ______________________________________                                    

EXAMPLE XI

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 20% Er₂ O₃ 15.5% Dy₂ O₃, 23.0% SiO₂, 25.0% B₂ O₃, 12.0% Al₂ O₃, 4.5% ZrO₂ and 0.1% CuO [wt. %]. The filter has an optical density of 4.0 at 4.5 mm thickness, and is color corrected for source F₃. This filter has the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   29.6   26.8   24.3 25.0 32.6  35.1 25.1 20.2                           Y.sub.AR (%)                                                                           34.1   30.9   28.0 28.9 37.6  40.5 28.9 23.3                           ______________________________________                                    

EXAMPLE XII

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 36.0% Er₂ O₃, 23.0% SiO₂, 25.0% B₂ O₃, 11.0% Al₂ O₃ and 5.0% ZrO₂, laminated to a glass containing 35.0% Sm₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃ and 2.0 ZrO₂ %, with an anti-reflective coating. The filter has an optical density of 4.0 at 4.1 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y.sub.AR (%)                                                                           53.3   46.7   44.9 43.1 55.1  59.7 43.1 39.5                           ______________________________________                                    

EXAMPLE XIII

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 34.0% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 11.0% Al₂ O₃ and 3.0% ZrO₂, laminated to a glass containing 35.0% Dy₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃ and 2.0% ZrO₂, with an anti-reflective coating. It has an optical density of 4.0 at 3.7 mm thickness. This filter is color balanced for all fluorescent sources without the addition of additional colorants and has the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y.sub.AR (%)                                                                           23.1   20.8   23.8 19.8 19.2  19.3 21.4 37.0                           ______________________________________                                    

EXHIBIT XIV

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 14% Nd₂ O₃ incorporated with 22% Dy₂ O₃, 25.0% SiO₂, 23.0% B₂ O₃, 13.0% Al₂ O₃, 3.0% ZrO₂, 0.029 CuO [wt. %]. It has an optical density of 4.0 at 4.5 mm thickness and is color balanced for all fluorescent sources. This filter has the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   14.5   13.7   15.3 13.2 13.3  13.2 14.6 25.4                           Y.sub.AR (%)                                                                   ______________________________________                                    

EXAMPLE XV

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 34.0% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 11.0% Al₂ O₃, and 3.0% ZrO₂, laminated to a glass containing, in mole percent, 35% Sm₂ O₃, 24.0% SiO₂, 24.0% B₂ O₃, 15.0% Al₂ O₃ and 2.0% ZrO₂, with an anti-reflective coating. It has an optical density of 4.0 at 3.3 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y.sub.AR (%)                                                                           22.1   19.4   22.2 18.2 18.0  18.3 19.8 35.5                           ______________________________________                                    

EXAMPLE XVI

A filter element for 532 nm radiation was made. It includes, in mole percent, the following: 35% Er₂ O₃, 25.0% SiO₂, 23.0% B₂ O₃, 13.0% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. It has an optical density of 4.0 at 2.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   50.9   45.4   44.0 42.4 53.1  57.2 42.2 36.9                           ______________________________________                                    

EXAMPLE XVII

A filter element for 532 nm and 1064 nm radiation. It includes, in mole percent, the following: 13% Nd₂ O₃ incorporated with 21% Dy₂ O₃, 25.25% SiO₂, 22.75% B₂ O₃, 14.0% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. The filter has an optical density of 4.0 at 4.0 mm thickness, and is color corrected for all fluorescent sources. This filter has the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.3   18.5   20.8 17.6 17.5  17.7 18.7 29.4                           ______________________________________                                    

EXAMPLE XVIII

A filter element for 532 nm radiation was made. It includes, in mole percent, the following: 34% Nd₂ O₃, 25.25% SiO₂, 22.75% B₂ O₃, 14.0% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. The filter has an optical density of 4.0 at 1.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.3   18.7   21.2 17.9 17.5  17.6 19.0 30.2                           ______________________________________                                    

EXAMPLE XIX

A filter element for 1064 nm radiation is made. It includes, in mole percent, the following: 33.0% Dy₂ O₃, 25.5% SiO₂, 23.5% B₂ O₃, 14.0% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. The filter has an optical density of 4.0 at 2.5 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   84.4   83.2   82.9 82.7 83.9  84.5 82.9 83.5                           ______________________________________                                    

EXAMPLE XX

A filter element for 1064 nm radiation is made. It includes, in mole percent, the following: 34.0% Sm₂ O₃, 25.25% SiO₂, 22.75% B₂ O₃, 14.0% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. The filter has an optical density of 4.0 at 1.8 mm thickness, with the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   79.9   77.6   77.1 76.7 79.0  80.0 77.3 80.3                           ______________________________________                                    

EXAMPLE XXI

A filter element for 532 nm and 1064 nm radiation is made. It includes, in mole percent, the following: 16.8% Nd₂ O₃ incorporated with 15.8% Sm₂ O₃, 26.0% SiO₂, 22.4% B₂ O₃, 15.2% Al₂ O₃, 3.0% ZrO₂ and 1.0% ZnO. The filter has an optical density of 4.0 at approximately 3.0 mm thickness, and is color balanced for all fluorescent sources. This filter has the following luminous transmission.

    ______________________________________                                         SOURCE  A      B      C    D.sub.65                                                                            F.sub.2                                                                              F.sub.3                                                                             F.sub.7                                                                             F.sub.11                       ______________________________________                                         Y (%)   20.2   18.1   20.4 17.1 17.2  17.5 18.2 28.4                           ______________________________________                                    

EXAMPLE XXII

A filter element for 532 nm is made. It includes, in mole percent, the following: 31.0% Er₂ O₃, 21.5% SiO₂, 22.5% B₂ O₃, 5.0% ZrO₂, 5% Y₂ O₃ and 15% Al₂ O₃.

EXAMPLE XXIII

A filter element for 532 nm is made. It includes, in mole percent, the following: 30.0% Er₂ O₃, 22.5% SiO₂, 22.5% B₂ O₃, 5.0% ZrO₂, 5.0% Y₂ O₃ and 15% Al₂ O₃.

EXAMPLE XXIV

A filter element for 532 nm is made. It includes, in mole percent, the following: 25.0% Er₂ O₃, 20.0% SiO₂, 20.0% B₂ O₃, 7.0% Zr₂ O₃, 7.0% Y₂ O₃ and 21.0% Al₂ O₃.

EXAMPLE XXV

A filter element for 532 nm is made. It includes, in mole percent, the following: 28.0% Er₂ O₃, 31.0% SiO₂, 21.0% B₂ O₃, 5.0% Zr₂ O₃ and 15.0% Al₂ O₃.

EXAMPLE XXVI

A filter element for 532 nm is made. It includes, in mole percent, the following: 32.0% Er₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 4.0% ZrO₂ and 12.0% Al₂ O₃.

EXAMPLE XXVII

A filter element for 532 nm is made. It includes, in mole percent, the following: 34.0% Er₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 3.0% ZrO₂ and 11.0% Al₂ O₃.

EXAMPLE XXVIII

A filter element for 532 nm is made. It includes, in mole percent, the following: 3.60% Er₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 2.0% ZrO₂ and 10.0% Al₂ O₃.

EXAMPLE XXIX

A filter element for 532 nm is made. It includes, in mole percent, the following: 34.0% Nd₂ O₃, 26.0% SiO₂, 26.0% B₂ O₃, 3.0% ZrO₂ and 11.0% Al₂ O₃.

EXAMPLE XXX

A filter element for 532 nm is made. It includes, in mole percent, the following: 33.0% Nd₂ O₃, 25.0% SiO₂, 25.0% B₂ O₃, 3.0% ZrO₂ and 14.0% Al₂ O₃.

EXAMPLE XXXI

A filter element for 532 nm is made. It includes, in mole percent, the following: 35.0% Nd₂ O₃, 24.0% SiO₂, 22.0% B₂ O₃, 3.0% ZrO₂ and 16.0% Al₂ O₃.

EXAMPLE XXXII

A filter element for 532 nm is made. It includes, in mole percent, the following: 28.0% Nd₂ O₃, 25.0% SiO₂, 25.0% B₂ O₃, 3.0% ZrO₂, 14.0% Al₂ O₃ and 5.0% Pr₂ ₃.

EXAMPLE XXXIII

A filter element for 532 nm is made. It includes, in mole percent, the following: 30.0% Nd₂ O₃, 25.0% SiO₂, 25.0% B₂ O₃, 3.0% ZrO₂, 14.0% Al₂ O₃ and 3.0% Pr₂ O₃.

EXAMPLE XXXIV

A filter element for 532 nm is made. It includes, in mole percent, the following: 33.0% Er₂ O₃, 25.5% SiO₂, 25.5% B₂ O₃, 3.0% ZrO₂, 12.0% Al₂ O₃ and 1.0% Pr₂ O₃.

EXAMPLE XXXV

A filter element for 532 nm is made. It includes, in mole percent, the following: 32.3% Er₂ O₃, 25.3% SiO₂, 25.3% B₂ O₃, 3.0% ZrO₂, 12.1% Al₂ O₃ and 0.64% Pr₂ O₃.

While embodiments and applications of this invention have been shown and described, it would be apparent to those skilled in the art that many more modifications than mentioned above are possible without departing from the inventive concepts herein. The invention, therefore, is not to be restricted except in the spirit of the appended claims. 

What is claimed is:
 1. A filter element consisting essentially of, in mole percent, 19-31% SiO₂, 19-31% B₂ O₃, 10-20% Al₂ O₃, 2-10% ZrO₂, 0-10% Y₂ O₃, and 25-39% of one or more rare earth oxides selected from the group Er₂ O₃, Nd₂ O₃, Dy₂ O₃, Sm₂ O₃, Ce₂ O₃, Pr₂ O₃, Ho₂ O₃, Yb₂ O₃ and Tm₂ O₃.
 2. The filter element of claim 1, wherein the rare earth oxides are selected from the group Er₂ O₃,Nd₂ O₃, DY₂ O₃ and Sm₂ O₃.
 3. The filter element of claim 1, wherein the ratio of SiO₂ to B₂ O₃ is about 0.8 to 1.4.
 4. The filter element of claim 1, wherein the amount of SiO₂ and B₂ O₃ is greater than about 40%.
 5. The filter element of claim 1, wherein the amount of Al₂ O₃, ZrO₂ and Y₂ O₃ is greater than about 12%.
 6. The filter element of claim 1 and further including one or more color correction oxides in an amount sufficient to provide a neutral glass, selected from the group consisting of Cr₂ O₃, Pr₂ O₃, Fe₂ O₃, CuO, NiO, V₂ O₅, Co₃ O₄ and Ti₂ O₃.
 7. The filter element of claim 6, wherein the color correction oxide is Pr₂ O₃.
 8. The filter element of claim 1, wherein the filter is an absorption filter for 532 nm.
 9. The filter element of claim 8, wherein the filter has an optical density of about 3.0 to 6.0.
 10. The filter element of claim 8, wherein the filter has a thickness of about 1.5 to 5.5 mm.
 11. The filter element of claim 1, wherein the filter is an absorption filter for 1064 nm.
 12. The filter element of claim 11, wherein the filter has an optical density of about 3.0 to 6.0.
 13. The filter element of claim 11, wherein the filter has a thickness of about 1.5 to 5.5 mm.
 14. The filter element of claim 1, wherein the filter is an absorption filter for 532 nm and 1064 nm.
 15. The filter element of claim 14, wherein the filter has an optical density of about 3.0 to 6.0 mm.
 16. The filter element of claim 14, wherein the filter has a thickness of about 1.5 to 5.5 mm.
 17. The filter element of claim 1, wherein the amount of rare earth oxides is greater than about 30 and but no greater than 39 mole percent.
 18. The filter element of claim 1, further including FeO in an amount of about 0.1 to 5.0 mole percent, and ZnO in an amount of about 0.1 to 5.0 mole percent.
 19. The filter element of claim 1, wherein the rare earth oxide is Er₂ O₃,and the resulting filter has a luminous transmission of greater than about 50%.
 20. The filter element of claim 1, wherein the rare earth oxide is either Dy₂ O₃ or Sm₂ O₃, and the resulting filter has a luminous transmission of greater than about 75%.
 21. The filter element of claim 1, wherein the rare earth oxide is Nd₂ O₃, and the resulting filter has a luminous transmission of greater than about 25%.
 22. The filter element of claim 1, wherein the rare earth oxides are Er₂ O₃ and Dy₂ O₃.
 23. The filter element of claim 1, wherein the rare earth oxides are Er₂ O₃ and Sm₂ O₃.
 24. The filter element of claim 1, wherein the rare earth oxides are Er₂ O₃ and Nd₂ O₃.
 25. The filter element of claim 1, wherein the rare earth oxides are Nd₂ O₃ and Dy₂ O₃.
 26. A glass composition consisting essentially of, by mole percent, 19-31% SiO₂, 19-31% B₂ O₃, 10-20% Al₂ O₃, 2-10% ZrO₂, 0-10% Y₂ O₃, and 25-39% of one or more rare earth oxides selected from the group Er₂ O₃, Nd₂ O₃, Dy₂ O₃, Sm₂ O₃, Ce₂ O₃, Pr₂ O₃, Ho₂ O₃, Tm₂ O₃, La₂ O₃, Gd₂ O₃ and Yb₂ O₃.
 27. The glass composition of claim 26, wherein the rare earth oxides are selected from the group Er₂ O₃,Nd₂ _(O) ₃, Dy₂ O₃ and Sm₂ O₃.
 28. The glass composition of claim 26, wherein the ratio of SiO₂ to B₂ O₃ is about 0.8 to 1.4.
 29. The glass composition of claim 26, where the amount of SiO₂ and B₂ O₃ are greater than about 40%.
 30. The glass composition of claim 26, wherein the amount of Al₂ O₃, ZrO₂ and Y₂ O₃ are greater than about 12%.
 31. The glass composition of claim 26, further including one or more color correction oxides in an amount sufficient to provide a neutral glass, selected from the group consisting of Cr₂ O₃, Pr₂ O₃, Fe₂ O₃, CuO, NiO, V₂ O₅, Co₃ O₄ and Ti₂ O₃.
 32. The glass composition of claim 31, wherein the color correction oxide is Pr₂ O₃.
 33. The glass composition of claim 26, wherein the mole percent of rare earth oxides is about 31-39%.
 34. The glass composition of claim 26, further including 0.1 to 5.0 mole percent FeO, and 0.1 to 5.0 mole percent ZnO.
 35. The glass composition of claim 26, wherein the rare earth oxides are Er₂ O₃ and Dy₂ O₃.
 36. The glass composition of claim 26, wherein the rare earth oxides are Er₂ O₃ and Sm₂ O₃.
 37. The glass composition of claim 26, wherein the rare earth oxides are Er₂ O₃ and Nd₂ O₃.
 38. The glass composition of claim 26, wherein the rare earth oxides are Nd₂ O₃ and Dy₂ O₃.
 39. The filter element of claim 1, wherein the rare earth oxides are selected from the group Er₂ O₃, Nd₂ O₃, Dy₂ O₃, Sm₂ O₃, Ce₂ O₃, Pr₂ O₃, and Ho₂ O₃.
 40. The glass composition of claim 26, wherein the rare earth oxides are selected from the group Er₂ O₃, Nd₂ O₃, Dy₂ O₃, Sm₂ O₃, Ce₂ O₃, Pr₂ O₃, and Ho₂ O₃. 